PA66 2103T Pingdingshan Shenma

ویژگی‌ها:
High modulus toughening type high temperature resistance high impact resistance
کاربردها:
Used for railway fender seats pipe fittings and sports equipment
مقایسه

برگه داده فنی

Other performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	平行，-	-	1.10 %
Shrinkage rate	Shrinkage rate	垂直，-	-	1.20 %
UL flame retardant rating		UL 94	--
density		ISO 1183	1.12
Water absorption rate	23℃Saturation	ISO 62	-- %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	Dry	ISO 527	2.1 GPa
Impact strength of cantilever beam gap	Dry	ISO 180	63.9 KJ/m
bending strength	Dry	ISO 178	64.6 MPa
tensile strength	Dry	ISO 527	60.3 MPa
Elongation at Break	Dry	ISO 527	26.2 %
Bending modulus	Dry	ISO 178	1.4 GPa
Charpy Notched Impact Strength	Dry	ISO 179	不断 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Dry	ISO 179	72.8 KJ/m

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	Dry	ISO 1133	15.8 g/10min
Linear coefficient of thermal expansion		ISO 11359	80 10
Hot deformation temperature	1.80MPa	ISO 75	66.4 ℃
Melting temperature	Dry	ISO 3146	246-255 ℃

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	Dry/湿态	IEC 93	-- Ω.cm
Dielectric strength	Dry	IEC 243	-- Kv/mm