برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.45 g/cm³ |
| Shrinkage rate | 横向流量 | 内部方法 | 0.30 - 0.70 % |
| Shrinkage rate | 流量 | 内部方法 | 0.10 - 0.40 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.020 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 10500 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 110 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | | ISO 178 | 10300 Mpa |
| bending strength | | ISO 178 | 170 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 26 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | > 1.0E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 35 KV/mm |
| dielectric constant | 1 MHz | IEC 60250 | 3.00 |
| Dissipation Factor | 1 MHz | IEC 60250 | 2.0E-3 |
| arc resistance | | ASTM D495 | PLC 6 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 2 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 3.0 to 5.0 hr |
| Processing (melt) temperature | | | 280 to 310 °C |
| Temperature | | | 130 to 155 °C |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 265 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 230 °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | TMA | 1.9E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | TMA | 4.2E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 130 °C |
| RTI Imp | | UL 746 | 120 °C |
| RTI | | UL 746 | 130 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.