SPS S931 BK IDEMITSU JAPAN
XAREC™ 
Electrical applications,Household daily necessities
Glass fiber reinforced,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B265 °C
1.8 MPa, UnannealedISO 75-2/A230 °C
Linear coefficient of thermal expansionAcross Flow : -30 to 30°CTMA4.2E-5 cm/cm/°C
Flow : -30 to 30°CTMA1.9E-5 cm/cm/°C
RTIUL 746130 °C
RTI ElecUL 746130 °C
RTI ImpUL 746120 °C
mechanical propertiesTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
Bending modulusISO 17810300 Mpa
bending strengthISO 178170 Mpa
Tensile modulusISO 527-210500 Mpa
Tensile strainBreakISO 527-21.5 %
tensile strengthBreakISO 527-2110 Mpa
Electrical performanceTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
Arc resistanceASTM D495PLC 6
Compared to the anti leakage trace indexIEC 60112PLC 1
Dielectric constant1 MHzIEC 602503.00
Dielectric strengthASTM D14935 KV/mm
Dissipation factor1 MHzIEC 602502.0E-3
High arc combustion index1.5 mmUL 746PLC 0
0.75 mmUL 746PLC 0
High voltage arc tracing rateUL 746PLC 3
Hot wire ignition0.75 mmUL 746PLC 3
1.5 mmUL 746PLC 2
Volume resistivityIEC 60093> 1.0E+16 ohms·cm
Physical propertiesTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
densityISO 11831.45 g/cm³
Shrinkage rateFlowInternal Method0.10 - 0.40 %
横向FlowInternal Method0.30 - 0.70 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.020 %
impact performanceTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
Charpy Notched Impact Strength23°CISO 1799.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 1808.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 17928 kJ/m²
Suspended wall beam without notch impact strength23°CISO 18026 kJ/m²
flammabilityTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
UL flame retardant rating 0.75 mmUL 94V-0
injectionTest ConditionTest MethodIDEMITSU JAPAN/S931 BK
drying temperature120 °C
drying time3.0 to 5.0 hr
Mold temperature130 to 155 °C
Processing (melt) temperature280 to 310 °C