HDPE PRE-ELEC® PE 1294 Premix Oy

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-20°C	ASTM D256	8.4 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	12 kJ/m²
Suspended wall beam without notch impact strength	-20°C,4.00mm	ASTM D256	NoBreak
	Suspended wall beam without notch impact strength	23°C,4.00mm	ASTM D256	NoBreak
		Suspended wall beam without notch impact strength	-20°C	ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ASTM D256	NoBreak
Impact strength of cantilever beam gap	-20°C,4.00mm，Area	ASTM D256	4.20 kJ/m²
	Impact strength of cantilever beam gap	23°C,4.00mm，Area	ASTM D256	12.6 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20°C	ISO 180	4.0 kJ/m²
Charpy Notched Impact Strength	-20°C	ISO 179	10 kJ/m²
	Charpy Notched Impact Strength	23°C	ISO 179	15 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ASTM D256	15 kJ/m²
Impact strength of simply supported beam without notch	-20°C	ASTM D256	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-20°C	ISO 179	NoBreak

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Bending modulus	4.00mm	ISO 178	1000 MPa
tensile strength	Yield	ASTM D638	23.0 MPa
	tensile strength	Yield	ISO 527-2	23.0 MPa
	tensile strength	tensile strength	4.00mm	ISO 527-2	12.0 MPa
elongation	Yield	ASTM D638	15 %
Tensile strain	Yield	ISO 527-2	15 %
elongation	Break	ASTM D638	300 %
Tensile strain	Break,4.00mm	ISO 527-2	300 %
Bending modulus	4.00mm	ASTM D790	1000 MPa
tensile strength		ASTM D638	12.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/Bf	76.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648A	45.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	45.0 °C
Vicat softening temperature	--	ISO 306/A50	125 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	63.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648B	76.1 °C
Vicat softening temperature	--	ASTM D15253	125 °C
Vicat softening temperature	Vicat softening temperature	--	ASTM D15254	62.8 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	0.996 g/cm³
density	density		ISO 1183	1.01 g/cm³
melt mass-flow rate	190°C/10.0kg	ASTM D1238	20 g/10min
	melt mass-flow rate	190°C/2.16kg	ASTM D1238	2.0 g/10min
		melt mass-flow rate	190°C/21.6kg	ASTM D1238	80 g/10min
			melt mass-flow rate	190°C/10.0kg	ISO 1133	20 g/10min
				melt mass-flow rate	190°C/2.16kg	ISO 1133	2.0 g/10min
				melt mass-flow rate	melt mass-flow rate	190°C/21.6kg	ISO 1133	80 g/10min
Shrinkage rate	MD	ASTM D955	1.5to2.5 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.5to2.5 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		ESDSTM11.11	<1.0E+5 ohms
Surface resistivity	Surface resistivity		IEC 61340-2-3	<1.0E+5 ohms
Volume resistivity		Internal Method	<1.0E+4 ohms·cm

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreA	ASTM D2240	95
	Shore hardness	ShoreD	ASTM D2240	66
		Shore hardness	ShoreA	ISO 868	95
		Shore hardness	Shore hardness	ShoreD	ISO 868	66