TPE DuraGrip® DGR 6070NC USA Advanced

مقایسه

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
Permanent compression deformation	70°C,22hr	ISO 815	45 %
Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	72 %
elongation	Break	ASTM D412	370 %
elongation	elongation	Break,23°C	ISO 37	370 %
Stretch permanent deformation	100%Strain	ASTM D412	15 %
tensile strength	100%Strain	ASTM D412	1.67 MPa
	tensile strength	100%Strain,23°C	ISO 37	1.67 MPa
		tensile strength	Yield,23°C	ASTM D412	7.83 MPa
		tensile strength	tensile strength	Yield,23°C	ISO 37	7.83 MPa
tear strength	24°C	ASTM D624	26.1 kN/m
Permanent compression deformation	24°C,22hr	ASTM D395B	27 %
	Permanent compression deformation	70°C,22hr	ASTM D395B	45 %
		Permanent compression deformation	100°C,22hr	ASTM D395B	72 %
		Permanent compression deformation	Permanent compression deformation	24°C,22hr	ISO 815	27 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	10.0 mg

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Brittle temperature		ASTM D746	-65.0 °C
Brittle temperature	Brittle temperature		ISO 812	-65.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
MeltViscosity	190°C,300sec^-1	ASTM D3835	104 Pa·s
density		ASTM D792	0.988 g/cm³
density	density		ISO 1183	0.988 g/cm³
Shrinkage rate	MD：1.59mm	ASTM D955	2.1 %
	Shrinkage rate	MD：3.18mm	ASTM D955	1.3 %
		Shrinkage rate	TD：1.59mm	ASTM D955	1.1 %
			Shrinkage rate	TD：3.18mm	ASTM D955	1.2 %
				Shrinkage rate	TD:1.59mm	ISO 294-4	1.1 %
					Shrinkage rate	MD:1.59mm	ISO 294-4	2.1 %
						Shrinkage rate	TD:3.18mm	ISO 294-4	1.2 %
						Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreA,5Sec	ASTM D2240	68
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 868	68

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile stress change rate	70°C,168hr，Break	ISO 1817	2.0 %
Tensile stress change rate	Tensile stress change rate	100°C,168hr，Break	ISO 1817	3.0 %
Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	9.0 %
Volume change	Volume change	100°C,168hr,inASTM#1Oil	ASTM D471	2.0 %
Change rate of tensile strength in air	70°C,168hr	ASTM D573	-9.0 %
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	-4.0 %
Volume change	100°C,168hr,在水中	ISO 1817	-7.0 %
	Volume change	100°C,168hr,inASTM#1Oil	ISO 1817	2.0 %
	Volume change	Volume change	100°C,168hr,inIRM903Oil	ISO 1817	38 %
Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	-4.0 %
	Change rate of tensile strength in air	100°C,168hr	ISO 188	-11 %
	Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	-2.0 %
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	2.0 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	3.0 %
Volume change	100°C,168hr,inIRM903Oil	ASTM D471	38 %
	Volume change	100°C,168hr,在水中	ASTM D471	-7.0 %
	Volume change	Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	9.0 %
Change rate of tensile strength in air	100°C,168hr	ASTM D573	-11 %
	Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	-2.0 %
	Change rate of tensile strength in air	Change rate of tensile strength in air	70°C,168hr	ISO 188	-9.0 %