ABS MAGNUM™ 3404 Trinseo
0
- کاربردها:TrinseoAmerican Jubilee
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Water absorption rate | Equilibrium | ISO 622 | 0.10 % |
| density | ISO 1183/B | 1.05 g/cm³ | |
| ISO 11832 | 1050 kg/m³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 6.6 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 6.70 cm³/10min |
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.70 % |
| Water absorption rate | Saturation | ISO 622 | 0.50 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| burning rate | 2.00mm | ISO 3795 | 50 mm/min |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 3.0mm | UL 94 | HB | |
| 1.50mm | ISO 12102 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile strain | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 2.7 % |
| Nominal fracture strain | ISO 527-22 | 40 % | |
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 2100 MPa |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 70.0 MPa |
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 2150 MPa |
| ISO 527-22 | 2150 MPa | ||
| tensile strength | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 43.0 MPa |
| Yield | ISO 527-22 | 43.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C,注塑 | ISO 179/2C | 8.0 kJ/m² |
| -30°C,注塑 | ISO 179/1eA | 13 kJ/m² | |
| 23°C,注塑 | ISO 179/1eA | 18 kJ/m² | |
| 23°C,注塑 | ISO 179/2C | 13 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C,注塑 | ISO 180/A | 11 kJ/m² |
| 23°C,注塑 | ISO 180/A | 19 kJ/m² | |
| 23°C | ISO 8256/12 | 68.0 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU2 | NoBreak |
| -30°C | ISO 179/1eU2 | NoBreak |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| relative permittivity | 100Hz | IEC 602502 | 2.80 |
| 1MHz | IEC 602502 | 2.80 | |
| Dissipation Factor | 100Hz | IEC 602502 | 6E-03 |
| 1MHz | IEC 602502 | 6E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 7E-05 cm/cm/°C |
| TD | ISO 11359-22 | 6.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 104 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 101 °C | |
| 1.8MPa，HDT | ISO 75-22 | 101 °C | |
| vicat | ISO 306/B50 | 102 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
تماس با ما
دریافت اپلیکیشن
Top