ABS MAGNUM™ 3404 Trinseo
--
Trinseo, American Jubilee
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO 8256/12 | 68.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C,注塑 | ISO 179/2C | 13 kJ/m² |
| 23°C,注塑 | ISO 179/1eA | 18 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C,注塑 | ISO 180/A | 11 kJ/m² |
| 23°C,注塑 | ISO 180/A | 19 kJ/m² | |
| Charpy Notched Impact Strength | -30°C,注塑 | ISO 179/2C | 8.0 kJ/m² |
| -30°C,注塑 | ISO 179/1eA | 13 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| Flexural modulus | 3.20mm,InjectionMolded | ISO 178 | 2100 MPa |
| bending strength | 3.20mm,InjectionMolded | ISO 178 | 70.0 MPa |
| Tensile modulus | 3.20mm,注塑 | ISO 527-2 | 2150 MPa |
| ISO 527-22 | 2150 MPa | ||
| Nominal fracture strain | ISO 527-22 | 40 % | |
| tensile strength | 屈服 | ISO 527-22 | 43.0 MPa |
| Tensile strain | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 2.7 % |
| tensile strength | Yield,3.20mm,InjectionMolded | ISO 527-2/50 | 43.0 MPa |
| Electrical performance | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| relative permittivity | 1MHz | IEC 602502 | 2.80 |
| Dissipation Factor | 1MHz | IEC 602502 | 6E-03 |
| 100Hz | IEC 602502 | 6E-03 | |
| relative permittivity | 100Hz | IEC 602502 | 2.80 |
| flammability | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| burning rate | 2.00mm | ISO 3795 | 50 mm/min |
| UL flame retardant rating | 1.50mm | ISO 12102 | HB |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 6.70 cm³/10min |
| Water absorption rate | 饱和 | ISO 622 | 0.50 % |
| Shrinkage rate | MD | ISO 294-4 | 0.40to0.70 % |
| density | ISO 1183/B | 1.05 g/cm³ | |
| ISO 11832 | 1050 kg/m³ | ||
| Water absorption rate | 平衡 | ISO 622 | 0.10 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 6.6 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/MAGNUM™ 3404 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ISO 11359-22 | 6.5E-05 cm/cm/°C |
| MD | ISO 11359-22 | 7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 101 °C |
| vicat | ISO 306/B50 | 102 °C | |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 101 °C |
| 0.45MPa，HDT | ISO 75-22 | 104 °C |