برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Apparent density | | ISO 60 | 0.60to0.80 g/cm³ |
| Shrinkage rate | MD2 | ISO 2577 | 0.50to0.90 % |
| Shrinkage rate | | ISO 2577 | 0.70to1.0 % |
| density | | ISO 1183 | 1.80to1.90 g/cm³ |
| Water absorption rate | 23°C,24hr | ISO 62 | <1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 900 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding pressure | | | >20.0 MPa |
| Compression molding temperature | | | 160to180 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| compression stress | | ISO 604 | 200to250 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 7000to9000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 8000to10000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 40.0to50.0 MPa |
| tensile strength | Injection | ISO 527-2 | 45.0to60.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 9000to11000 MPa |
| Flexural modulus | Injection | ISO 178 | 10000to12000 MPa |
| bending strength | Compression Molded | ISO 178 | 90.0to110 MPa |
| bending strength | Injection | ISO 178 | 100to120 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 1.5to3.0 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 2.5to4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 4.0to7.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 7.0to9.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+11到1.0E+12 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20to30 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 11.016.0 |
| relative permittivity | 1MHz | IEC 60250 | 7.009.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.20to0.40 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020to0.040 |
| arc resistance | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| maximum service temperature | 20,000h | IEC 60216 | 150 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 130to150 °C |
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.50to0.60 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 200 °C |