TPO

TPO PRE-ELEC® PP 1383 Premix Oy

0

برگه داده فنی

impact performanceشرایط آزمونروش آزموننتیجه آزمون
Impact strength of cantilever beam gap23°CISO 1809.0 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D25654.6 kJ/m²
Suspended wall beam without notch impact strength23°C,4.00mmASTM D25660.9 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 18055 kJ/m²
Suspended wall beam without notch impact strength23°CISO 18059 kJ/m²
Charpy Notched Impact Strength-20°CASTM D2568.4 kJ/m²
Charpy Notched Impact Strength-20°CISO 1799.0 kJ/m²
Charpy Notched Impact Strength23°CISO 17912 kJ/m²
Charpy Notched Impact Strength23°CASTM D25611 kJ/m²
Impact strength of simply supported beam without notch-20°CASTM D256NoBreak
Impact strength of simply supported beam without notch-20°CISO 179NoBreak
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Impact strength of simply supported beam without notch23°CASTM D256NoBreak
Impact strength of cantilever beam gap-20°C,4.00mm，AreaASTM D2564.20 kJ/m²
Impact strength of cantilever beam gap23°C,4.00mm，AreaASTM D2568.41 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1805.0 kJ/m²
mechanical propertiesشرایط آزمونروش آزموننتیجه آزمون
elongationBreakASTM D6385.0 %
tensile strengthASTM D63825.0 MPa
tensile strengthISO 527-225.0 MPa
Tensile strainBreakISO 527-25.0 %
Bending modulus4.00mmASTM D7901310 MPa
Bending modulus4.00mmISO 1781300 MPa
thermal performanceشرایط آزمونروش آزموننتیجه آزمون
Hot deformation temperature0.45MPa,UnannealedASTM D648B100 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/Bf100 °C
Vicat softening temperatureASTM D15253149 °C
Vicat softening temperatureISO 306/A50150 °C
Physical propertiesشرایط آزمونروش آزموننتیجه آزمون
melt mass-flow rate230°C/2.16kgISO 113314 g/10min
Shrinkage rateMDASTM D9551.2to1.4 %
Shrinkage rateMDISO 294-41.2to1.4 %
densityASTM D7920.996 g/cm³
densityISO 11830.990 g/cm³
melt mass-flow rate230°C/2.16kgASTM D123814 g/10min
Electrical performanceشرایط آزمونروش آزموننتیجه آزمون
Surface resistivityESDSTM11.11<1.0E+3 ohms
Surface resistivityIEC 61340-2-3<1.0E+3 ohms
Volume resistivityInternal Method<1.0E+2 ohms·cm
hardnessشرایط آزمونروش آزموننتیجه آزمون
Shore hardnessShoreAASTM D224095
Shore hardnessShoreDASTM D224065
Shore hardnessShoreAISO 86895
Shore hardnessShoreDISO 86865