PC LEXAN™ HP2-1H111 SABIC INNOVATIVE SINGAPHORE
56
- ویژگی‌ها:جریان بالا
- کاربردها:مراقبت های پزشکیداروها
مقایسه
مشاهده قیمتهابرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| 平衡,23°C | ASTM D570 | 0.35 % | |
| 平衡,100°C | ASTM D570 | 0.58 % | |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 18 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 16.0 cm3/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| R计秤 | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 25 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2370 Mpa | |
| ISO 527-2/1 | 2350 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂 | ASTM D638 | 68.0 Mpa | |
| 断裂 | ISO 527-2/50 | 65.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 130 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| ISO 178 | 2300 Mpa | ||
| bending strength | ISO 178 | 90.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 96.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 10.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| 23°C | ISO 180/1A | 12 kJ/m² | |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 62.0 J |
| 23°C | ASTM D3029 | 169 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm | ||
| dielectric strength | 3.20mm,inAir | ASTM D149 | 15 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| dielectric constant | 50Hz | ASTM D150 | 3.17 |
| 60Hz | ASTM D150 | 3.17 | |
| 1MHz | ASTM D150 | 2.96 | |
| relative permittivity | 50Hz | IEC 60250 | 2.70 |
| 60Hz | IEC 60250 | 2.70 | |
| 1MHz | IEC 60250 | 2.70 | |
| Dissipation Factor | 50Hz | ASTM D150 | 9E-04 |
| 60Hz | ASTM D150 | 9E-04 | |
| 1MHz | ASTM D150 | 0.010 | |
| 50Hz | IEC 60250 | 1E-03 | |
| 60Hz | IEC 60250 | 1E-03 | |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| ISO 8302 | 0.20 W/m/K | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 133 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 129 °C | |
| 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 122 °C | |
| vicat | ASTM D152510 | 154 °C | |
| -- | ISO 306/B50 | 140 °C | |
| -- | ISO 306/B120 | 141 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| specific heat | ASTMC351 | 1250 J/kg/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 137 °C |