Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HP2-1H111 SABIC INNOVATIVE SINGAPHORE
LEXAN™
medical care、medicine
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 10 kJ/m² |
| Falling hammer impact | 23°C | ASTMD3029 | 169 J |
| Suspended wall beam gap impact strength 7 | 23°C | ISO180/1A | 12 kJ/m² |
| Tensile impact strength 8 | ASTMD1822 | 546 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 62.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTMD785 | 118 |
| M计秤 | ASTMD785 | 70 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 63.0 Mpa |
| elongation | 断裂 | ASTMD638 | 130 % |
| Bending strength 5,6 | ISO178 | 90.0 Mpa | |
| Tensile modulus | ASTMD638 | 2370 Mpa | |
| Tensile strain | 屈服 | ISO527-2/50 | 6.0 % |
| Tensile stress | 断裂 | ISO527-2/50 | 65.0 Mpa |
| elongation | 屈服 | ASTMD638 | 7.0 % |
| Tensile modulus | ISO527-2/1 | 2350 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 62.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTMD790 | 96.0 Mpa |
| tensile strength | 断裂 | ASTMD638 | 68.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 100 % |
| Flexural modulus | ISO178 | 2300 Mpa | |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg | |
| Flexural modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| 50Hz | IEC60250 | 2.70 | |
| Volume resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| dielectric constant | 1MHz | ASTMD150 | 2.96 |
| 50Hz | ASTMD150 | 3.17 | |
| Dissipation Factor | 60Hz | ASTMD150 | 9E-04 |
| 50Hz | ASTMD150 | 9E-04 | |
| 1MHz | ASTMD150 | 0.010 | |
| dielectric constant | 60Hz | ASTMD150 | 3.17 |
| Dissipation Factor | 60Hz | IEC60250 | 1E-03 |
| 50Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 0.010 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 2 |
| 60Hz | IEC60250 | 2.70 | |
| 1MHz | IEC60250 | 2.70 | |
| High arc combustion index (HAI) | HAI | UL746 | PLC 1 |
| dielectric strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 3.20mm,inAir | ASTMD149 | 15 KV/mm |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| refractive index | ASTMD542 | 1.586 | |
| transmissivity | 2540µm | ASTMD1003 | 88.0 % |
| Haze ratio | 2540µm | ASTMD1003 | 1.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Limiting Oxygen Index | ISO4589-2 | 25 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.35 % |
| 24hr | ASTMD570 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 18 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 16.0 cm3/10min |
| Water absorption rate | 平衡,100°C | ASTMD570 | 0.58 % |
| Specific volume | ASTMD792 | 0.830 cm³/g |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SINGAPHORE/HP2-1H111 |
|---|---|---|---|
| BallPressure Test | 125°C | IEC60695-10-2 | Pass |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 129 °C | |
| RTI Imp | UL746 | 130 °C | |
| vicat | -- | ISO306/B50 | 140 °C |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 137 °C | |
| specific heat | ASTMC351 | 1250 J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 W/m/K | |
| MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C | |
| RTI Str | UL746 | 130 °C | |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 °C |
| RTI Elec | UL746 | 130 °C | |
| MD：23到80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 122 °C |
| vicat | -- | ISO306/B120 | 141 °C |
| thermal conductivity | ISO8302 | 0.20 W/m/K | |
| vicat | ASTMD152510 | 154 °C |