PP Homopolymer SAXALEN™ PPH335T20 SAX AUSTRIA

ویژگی‌ها:
Filler mineral filler 20% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	2.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	19 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	40 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	2.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	17 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	40 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ISO 527-2/1	3000 MPa
tensile strength	Break	ISO 527-2/50	37.0 MPa
Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ISO 178	2400 MPa
bending strength		ISO 178	42.0 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8MPa,Unannealed,60.0mmSpan	ISO 75-2/A	72.0 °C
Vicat softening temperature		ISO 306/B120	103 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	14.0 cm³/10min
density		ISO 1183	1.04 g/cm³