PP Homopolymer SAXALEN™ PPH335T20 SAX AUSTRIA
--
--
Filler, mineral filler, 20%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SAX AUSTRIA/SAXALEN™ PPH335T20 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 17 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 40 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 19 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SAX AUSTRIA/SAXALEN™ PPH335T20 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2400 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Tensile modulus | ISO 527-2/1 | 3000 MPa | |
| bending strength | ISO 178 | 42.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 37.0 MPa |
| physical property | Test Condition | Test Method | SAX AUSTRIA/SAXALEN™ PPH335T20 |
|---|---|---|---|
| density | ISO 1183 | 1.04 g/cm³ | |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 14.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | SAX AUSTRIA/SAXALEN™ PPH335T20 |
|---|---|---|---|
| vicat | ISO 306/B120 | 103 °C | |
| Heat distortion temperature | 1.8MPa,未退火,60.0mm跨距，HDT | ISO 75-2/A | 72.0 °C |