| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.45to1.47 g/cm³ |
| PVC unit classification | | ASTM D4216 | 1-43344-12 |
| density | | ASTM D792 | 1.45to1.47 g/cm³ |
| PVC unit classification | | ASTM D4216 | 1-43344-12 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| DurometerHardness | ShoreD,22°C | ASTM D2240 | 75to81 |
| DurometerHardness | ShoreD,22°C | ASTM D2240 | 75to81 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| burning rate | (AEB)Avg.ExtentofBurning | ASTM D635 | <5.00 mm |
| burning rate | (ATB)Avg.TimeofBurning:2.54mm | ASTM D635 | <5.0 sec |
| burning rate | (AEB)Avg.ExtentofBurning | ASTM D635 | <5.00 mm |
| burning rate | (ATB)Avg.TimeofBurning:2.54mm | ASTM D635 | <5.0 sec |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | 22°C | ASTM D790 | 2650 MPa |
| bending strength | 22°C | ASTM D790 | 80.0 MPa |
| Tensile modulus | 22°C | ASTM D638 | 3010 MPa |
| tensile strength | 屈服,22°C | ASTM D638 | 46.2 MPa |
| Flexural modulus | 22°C | ASTM D790 | 2650 MPa |
| bending strength | 22°C | ASTM D790 | 80.0 MPa |
| Tensile modulus | 22°C | ASTM D638 | 3010 MPa |
| tensile strength | 屈服,22°C | ASTM D638 | 46.2 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 22°C | ASTM D256 | 980 J/m |
| Dart impact | 22°C,Extrudedat370to380°Fmelttemperature2 | ASTM D4226 | >120 J/cm |
| Dart impact | 22°C,Extrudedat370to380°Fmelttemperature3 | ASTM D4226 | >120 J/cm |
| Impact strength of cantilever beam gap | 22°C | ASTM D256 | 980 J/m |
| Dart impact | 22°C,Extrudedat370to380°Fmelttemperature2 | ASTM D4226 | >120 J/cm |
| Dart impact | 22°C,Extrudedat370to380°Fmelttemperature3 | ASTM D4226 | >120 J/cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 70.6 °C |
| Linear coefficient of thermal expansion | MD：22°C | ASTM D696 | 5.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 70.6 °C |
| Linear coefficient of thermal expansion | MD：22°C | ASTM D696 | 5.2E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.