برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melt mass-flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| melt mass-flow rate | 220℃/10.0 kg | ASTM D1238 | 20 g/10 min |
| Shrinkage rate | MD | ASTM D955 | < 0.40 % |
| Water absorption rate | 饱和 | ASTM D570 | < 0.30 % |
| Shrinkage rate | MD | ASTM D995 | <0.40 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | <0.30 % |
| melt mass-flow rate | 200℃/5.0Kg | ASTM D1238 | 1.8 g/10min |
| melt mass-flow rate | 220℃/10.0Kg | ASTM D1238 | 20 g/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | | ASTM D785 | 115 R |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 屈服, 23℃ | ASTM D790 | 77.5 Mpa |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 200 J/m |
| Impact strength of cantilever beam gap | 23℃, 6.35 mm | ASTM D256 | 180 J/m |
| Rockwell hardness | R 级, 23℃ | ASTM D785 | 115 |
| tensile strength | 屈服, 23℃, 3.18 mm | ASTM D638 | 44.1 Mpa |
| tensile strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 37.3 Mpa |
| elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 30 % |
| elongation at break | 23°C | ASTM D638 | 30 % |
| bending strength | 23°C | ASTM D790 | 76 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2550 Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 220 J/m |
| tensile strength | 23°C | ASTM D638 | 44 Mpa |
| Flexural modulus | 23℃ | ASTM D790 | 27000 Mpa |
| Flame retardant performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL -94 | HB 1.50mm |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1E+22 Ω.cm |
| dielectric strength | | ASTM D149 | 22 KV/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 退火, 12.7 mm，HDT | ASTM D648 | 85 °C |
| vicat | | ASTM D1525 | 103 °C |
| High arc combustion index (HAI) | 1.57 mm | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | 1.57 mm | UL 746 | mm/min |
| Hot wire ignition (HWI) | 1.57 mm | UL 746 | PLC 3 sec |
| UL flame retardant rating | 1.59 mm | UL 94 | HB |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 85 °C |
| vicat | | ASTM1525 | 103 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.