PC LEXAN™ AD143-111 SABIC INNOVATIVE NETHERLANDS

ویژگی‌ها:
ثبات حرارتیدرخشش بالا
کاربردها:
لوازم خانگیروشناییکاربردهای الکتریکی
مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Refractive index		ISO 489	1.586
transmissivity	2540μm	ASTM D1003	89.0 %
turbidity	2540μm	ASTM D1003	<0.80 %

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	73 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	14 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	64.0 J

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
Burning wire flammability index	1.6mm	IEC 60695-2-12	850 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	--2	ASTM D638	2300 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350 Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	10.0 mg
bending strength	Yield,50.0mmSpan4	ASTM D790	97.0 Mpa
bending strength	bending strength	--5,6	ISO 178	90.0 Mpa
Bending modulus	--5	ISO 178	2300 Mpa
Bending modulus	Bending modulus	50.0mmSpan4	ASTM D790	2340 Mpa
elongation	Break	ISO 527-2/50	120 %
	elongation	Break3	ASTM D638	130 %
		elongation	Yield	ISO 527-2/50	6.0 %
		elongation	elongation	Yield3	ASTM D638	7.0 %
tensile strength	Break	ISO 527-2/50	70.0 Mpa
	tensile strength	Break3	ASTM D638	69.0 Mpa
		tensile strength	Yield	ISO 527-2/50	63.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	62.0 Mpa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature	--	ISO 306/B120	141 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	7E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23to80°C	ISO 11359-2	7E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.20 W/m/K
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan9	ISO 75-2/Be	135 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	114 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	130 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	123 °C
Vicat softening temperature	--	ASTM D152510	153 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	140 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Shrinkage rate	TD:3.20mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	12.0 cm3/10min
melt mass-flow rate	300°C/1.2kg	ASTM D1238	13 g/10min

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface resistivity		ASTM D257	5E+13 ohms

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Ball Pressure Test	H358/30	ISO 2039-1	95.0 Mpa