Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC AD143-111 SABIC INNOVATIVE NETHERLANDS
LEXAN™
household electrical appl、Casters、Electrical applications
Thermal stability、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 73 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 64.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 97.0 Mpa |
| Tensile modulus | --2 | ASTM D638 | 2300 Mpa |
| tensile strength | 屈服3 | ASTM D638 | 62.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 130 % |
| 断裂 | ISO 527-2/50 | 120 % | |
| Flexural modulus | --5 | ISO 178 | 2300 Mpa |
| 50.0mm跨距4 | ASTM D790 | 2340 Mpa | |
| bending strength | --5,6 | ISO 178 | 90.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 70.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| 屈服3 | ASTM D638 | 7.0 % | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 10.0 mg |
| tensile strength | 断裂3 | ASTM D638 | 69.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2350 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 5E+13 ohms |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | <0.80 % |
| refractive index | ISO 489 | 1.586 | |
| transmissivity | 2540µm | ASTM D1003 | 89.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 12.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NETHERLANDS/AD143-111 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 130 °C |
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距9，HDT | ISO 75-2/Ae | 123 °C |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 141 °C |
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| vicat | -- | ASTM D152510 | 153 °C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 140 °C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距9，HDT | ISO 75-2/Be | 135 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 114 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |