برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.35 g/cm³ |
| density | | ISO 11832 | 1340 kg/m³ |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 12.3 cm³/10min |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.0to3.0 % |
| Water absorption rate | Saturation | ISO 622 | 0.10 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 117 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | 1.70mm | ISO 12102 | V-0 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 69 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | 8.20 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 7.50 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU2 | 38.3 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | 35.9 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | 3.17mm | ASTM D790 | 5690 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 137 MPa |
| Tensile modulus | | ISO 527-22 | 6300 MPa |
| tensile strength | | ASTM D638 | 93.2 MPa |
| tensile strength | Break | ISO 527-22 | 96.0 MPa |
| elongation | Break | ASTM D638 | 4.0 % |
| Tensile strain | Break | ISO 527-22 | 1.8 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 600932 | >1.0E+15 ohms |
| Volume resistivity | | IEC 600932 | >1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-12 | 28 kV/mm |
| relative permittivity | 1MHz | IEC 602502 | 3.10 |
| Dissipation Factor | 1MHz | IEC 602502 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 601122 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 125 °C |
| Glass Transition Temperature | | ISO 11357-22 | 140 °C |
| vicat | 50N | ISO 3062 | 127 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 2.9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-22 | 6.2E-05 cm/cm/°C |
| RTI Elec | 1.7mm | UL 746 | 60.0 °C |
| RTI Imp | 1.7mm | UL 746 | 60.0 °C |
| RTI Str | 1.7mm | UL 746 | 60.0 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 135 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 120 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.