Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Lupoy® GP5206F LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 69 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA2 | 7.50 kJ/m² |
| 23°C | ISO 179/1eU2 | 38.3 kJ/m² | |
| -30°C | ISO 179/1eU2 | 35.9 kJ/m² | |
| 23°C | ISO 179/1eA2 | 8.20 kJ/m² |
| hardness | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 117 |
| Electrical performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| Volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| relative permittivity | 1MHz | IEC 602502 | 3.10 |
| Dissipation Factor | 1MHz | IEC 602502 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | IEC 601122 | PLC 3 | |
| Surface Resistivity | IEC 600932 | >1.0E+15 ohms | |
| dielectric strength | IEC 60243-12 | 28 kV/mm |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| Tensile modulus | ISO 527-22 | 6300 MPa | |
| tensile strength | ASTM D638 | 93.2 MPa | |
| Tensile strain | 断裂 | ISO 527-22 | 1.8 % |
| Flexural modulus | 3.17mm | ASTM D790 | 5690 MPa |
| tensile strength | 断裂 | ISO 527-22 | 96.0 MPa |
| bending strength | 屈服,3.17mm | ASTM D790 | 137 MPa |
| flammability | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| UL flame retardant rating | 1.70mm | ISO 12102 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| Water absorption rate | 饱和 | ISO 622 | 0.10 % |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 12.3 cm³/10min |
| density | ASTM D792 | 1.35 g/cm³ | |
| ISO 11832 | 1340 kg/m³ | ||
| Shrinkage rate | MD：3.18mm | ASTM D955 | 1.0to3.0 % |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® GP5206F |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 127 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-22 | 6.2E-05 cm/cm/°C |
| MD | ISO 11359-22 | 2.9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 120 °C |
| RTI Imp | 1.7mm | UL 746 | 60.0 °C |
| RTI Elec | 1.7mm | UL 746 | 60.0 °C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-22 | 125 °C |
| Glass Transition Temperature | ISO 11357-22 | 140 °C | |
| RTI Str | 1.7mm | UL 746 | 60.0 °C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 135 °C |