| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.4 % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.3 % |
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 3.0 % |
| Water absorption rate | 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.3 % |
| viscosity number | 96% H2SO4 | ISO 307 | 95.0 cm³/g |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 114 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 27 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 2400 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| Nominal tensile fracture strain | | ISO 527-2 | 17 % |
| Flexural modulus | | ISO 178 | 2100 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Filling analysis | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt density | | | 0.900 g/cm³ |
| Specific Heat Capacity of Melt | | | 2750 J/kg/°C |
| Thermal Conductivity of Melt | | | 0.18 W/m/K |
| Emission of Organic Compounds | | VDA 277 | 3.10 µgC/g |
| squeeze out | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 80 °C |
| drying time | | | 3.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.060 % |
| Melt Temperature | | | 235 to 250 °C |
| Extrusion Melt Temperature, Optimum | | | 240 °C |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 62631-3-1 | 1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-1 | 30 KV/mm |
| relative permittivity | 1 MHz | IEC 62631-2-1 | 3.20 |
| relative permittivity | 100 Hz | IEC 62631-2-1 | 3.60 |
| Dissipation Factor | 100 Hz | IEC 62631-2-1 | 0.014 |
| Dissipation Factor | 1 MHz | IEC 62631-2-1 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.15 % |
| Processing (melt) temperature | | | 230 to 290 °C |
| Melt Temperature, Optimum | | | 250 °C |
| Temperature | | | 50 to 90 °C |
| Mold Temperature, Optimum | | | 70 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | Drying Recommended | | yes |
| Hold Pressure Time | | | 4.00 s/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 135 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 62.0 °C |
| vicat | | ISO 306/B50 | 181 °C |
| melting temperature | | ISO 11357-3 | 218 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : -40 到 23°C | ISO 11359-2 | 9.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 流动 : 55 到 160°C | ISO 11359-2 | 1.6E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -40 到 23°C | ISO 11359-2 | 9.0E-5 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 55 到 160°C | ISO 11359-2 | 1.8E-4 cm/cm/°C |