| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 260°C/5.0 kg | ISO 1133 | 17.0 cm3/10min |
| Shrinkage rate | Flow | 内部方法 | 0.40 - 0.60 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.60 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 106 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| Burning wire flammability index | 3.2 mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 2500 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 55.0 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 60.0 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 62.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/5 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 130 % |
| Tensile strain | 断裂 | ISO 527-2/50 | > 50 % |
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ISO 178 | 85.0 Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 95.0 mg |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | > 1.0E+15 ohms·cm |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1 MHz | IEC 60250 | 2.80 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.013 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 100 to 110 °C |
| drying time | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Hopper temperature | | | 60 to 80 °C |
| Temperature at the rear of the barrel | | | 230 to 260 °C |
| Temperature in the middle of the barrel | | | 250 to 290 °C |
| Temperature at the front of the material cylinder | | | 250 to 290 °C |
| Spray nozzle temperature | | | 240 to 280 °C |
| Processing (melt) temperature | | | 260 to 290 °C |
| Temperature | | | 60 to 90 °C |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Be | 121 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距，HDT | ISO 75-2/Ae | 112 °C |
| vicat | -- | ISO 306/B50 | 129 °C |
| vicat | -- | ISO 306/B120 | 132 °C |
| Linear coefficient of thermal expansion | 23 到 60°C，流动 | ISO 11359-2 | 8.0E-5 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.