LLDPE Osterlene® LL01020SA OSTERMAN USA

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
turbidity		ASTM D1003	11 %
gloss	45°	ASTM D2457	30

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Vicat softening temperature		ASTM D1525	108 °C
Melting temperature		Internal Method	121 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	0.920 g/cm³
melt mass-flow rate	190°C/2.16kg	ASTM D1238	0.95 g/10min

film	شرایط آزمون	روش آزمون	نتیجه آزمون
film thickness			51 µm
Thin film puncture strength		Internal Method	18.0 J/cm³
Secant modulus	2%Secant,MD	ASTM D882	181 MPa
Secant modulus	Secant modulus	2%Secant,TD	ASTM D882	235 MPa
tensile strength	MD:Yield	ASTM D882	12.5 MPa
tensile strength	tensile strength	TD:Break	ASTM D882	44.5 MPa
elongation	MD:Break	ASTM D882	730 %
elongation	elongation	TD:Break	ASTM D882	810 %
Dart impact		ASTM D1709A	300 g
Elmendorf tear strength	MD	ASTM D1922	810 g
Elmendorf tear strength	Elmendorf tear strength	TD	ASTM D1922	1100 g
tensile strength	TD:Yield	ASTM D882	13.5 MPa
tensile strength	tensile strength	MD:Break	ASTM D882	52.0 MPa