LLDPE Osterlene® LL01020SA OSTERMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | OSTERMAN USA/Osterlene® LL01020SA |
|---|---|---|---|
| tensile strength | TD:断裂 | ASTM D882 | 44.5 MPa |
| elongation | MD:断裂 | ASTM D882 | 730 % |
| Dart impact | ASTM D1709A | 300 g | |
| Thin film puncture strength | 内部方法 | 18.0 J/cm³ | |
| tensile strength | MD:断裂 | ASTM D882 | 52.0 MPa |
| Secant modulus | 2%正割,TD | ASTM D882 | 235 MPa |
| Elmendorf tear strength | MD | ASTM D1922 | 810 g |
| Secant modulus | 2%正割,MD | ASTM D882 | 181 MPa |
| tensile strength | TD:屈服 | ASTM D882 | 13.5 MPa |
| film thickness | 51 µm | ||
| Elmendorf tear strength | TD | ASTM D1922 | 1100 g |
| tensile strength | MD:屈服 | ASTM D882 | 12.5 MPa |
| elongation | TD:断裂 | ASTM D882 | 810 % |
| optical performance | Test Condition | Test Method | OSTERMAN USA/Osterlene® LL01020SA |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 30 |
| Haze ratio | ASTM D1003 | 11 % |
| physical property | Test Condition | Test Method | OSTERMAN USA/Osterlene® LL01020SA |
|---|---|---|---|
| density | ASTM D792 | 0.920 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.95 g/10min |
| Thermal performance | Test Condition | Test Method | OSTERMAN USA/Osterlene® LL01020SA |
|---|---|---|---|
| vicat | ASTM D1525 | 108 °C | |
| melting temperature | 内部方法 | 121 °C |