PC TCL-1 MITSUBISHI RAYON AMERICA
0
- ویژگی‌ها:High resistance to low-temperature impact and heat resistance
- کاربردها:Application in the automotive field
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D-792 | 1.12 g/cm3 | |
| Shrinkage rate | MD | ASTM D-955 | 0.55 % |
| Water absorption rate | 24hr | ASTM D-570 | 0.20 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Rockwell hardness | ASTM D-785 | 105 R Scale | |
| tensile strength | 屈服 | ASTM D-638 | 43.1 MPa |
| elongation at yield | ASTM D-638 | 80 % | |
| Flexural modulus | ASTM D-790 | 1860 MPa | |
| bending strength | 屈服 | ASTM D-790 | 64.7 MPa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 400 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa，未退火，HDT | 109 | |
| melting temperature | 230-260 ℃ | ||
| Linear coefficient of thermal expansion | Flow | ASTM D-696 | 0.000085 cm/cm/℃ |
| UL flame retardant rating | 1.59mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa，未退火，HDT | ASTM D-648 | 128 ℃ |