Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC TCL-1 MITSUBISHI RAYON AMERICA
--
Application in the automotive field
High resistance to low-temperature impact and heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/TCL-1 |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D-638 | 43.1 MPa |
| Rockwell hardness | ASTM D-785 | 105 R Scale | |
| elongation at yield | ASTM D-638 | 80 % | |
| bending strength | 屈服 | ASTM D-790 | 64.7 MPa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D-256 | 400 J/m |
| Flexural modulus | ASTM D-790 | 1860 MPa |
| physical property | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/TCL-1 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D-570 | 0.20 % |
| density | ASTM D-792 | 1.12 g/cm3 | |
| Shrinkage rate | MD | ASTM D-955 | 0.55 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI RAYON AMERICA/TCL-1 |
|---|---|---|---|
| UL flame retardant rating | 1.59mm | UL 94 | HB |
| Linear coefficient of thermal expansion | 流动 | ASTM D-696 | 0.000085 cm/cm/℃ |
| melting temperature | 230-260 ℃ | ||
| Heat distortion temperature | 0.45MPa，未退火，HDT | ASTM D-648 | 128 ℃ |
| 1.8MPa，未退火，HDT | 109 |