PC+AS LNP™ LUBRICOMP™ Lexan_WR6300 compound SABIC

کاربردها:
Business equipment
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	2500 J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	60.2 J
Impact strength of cantilever beam gap	23°C	ASTM D4812	2500 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
		Impact strength of cantilever beam gap	23°C	ASTM D256	680 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	170 J/m

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.50mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Break	ASTM D638	160 %
Bending modulus	50.0mmSpan	ASTM D790	2490 MPa
bending strength	Yield,50.0mmSpan	ASTM D790	96.5 MPa
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
elongation	Break	ASTM D638	160 %
tensile strength	Yield	ASTM D638	60.7 MPa
tensile strength	tensile strength	Break	ASTM D638	61.4 MPa
Bending modulus	50.0mmSpan	ASTM D790	2490 MPa
bending strength	Yield,50.0mmSpan	ASTM D790	96.5 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
RTI		UL 746	80.0 °C
RTI Str		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Elec		UL 746	80.0 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Vicat softening temperature		ASTM D15254	137 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	134 °C
RTI Imp		UL 746	80.0 °C
RTI Elec		UL 746	80.0 °C
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	1.2E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	1.1E-04 cm/cm/°C
Vicat softening temperature		ASTM D15255	137 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	121 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	117 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.17 g/cm³
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70 %
density		ASTM D792	1.17 g/cm³
Melt Volume Flow Rate (MVR)	300°C/2.16kg	ISO 1133	38.0 cm³/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50to0.70 %