PA612 Generic Nylon 612 Generic

0

برگه داده فنی

physical property شرایط آزمونروش آزموننتیجه آزمون
density--ASTM D7921.03to1.35 g/cm³
density23°CISO 11831.06to1.07 g/cm³
Shrinkage rateMD:23°CASTM D9550.23to2.0 %
Shrinkage rateTD:23°CASTM D9551.1to2.0 %
Shrinkage rate23°CISO 294-41.1to1.8 %
Water absorption rate23°C,24hrASTM D5700.13to0.38 %
Water absorption rate饱和,23°CASTM D5703.0to4.0 %
Water absorption rate饱和,23°CISO 622.1to3.0 %
Water absorption rate平衡,23°C,50%RHISO 620.88to1.3 %
hardnessشرایط آزمونروش آزموننتیجه آزمون
Rockwell hardness23°CASTM D785108to115
flammabilityشرایط آزمونروش آزموننتیجه آزمون
Burning wire flammability indexIEC 60695-2-12719to725 °C
Hot filament ignition temperatureIEC 60695-2-13700to750 °C
Mechanical propertiesشرایط آزمونروش آزموننتیجه آزمون
bending strength23°CASTM D79023.0to296 MPa
bending strength23°CISO 17828.5to71.1 MPa
coefficient of frictionASTM D18940.13to1.0
Flexural modulus23°CISO 1781300to2110 MPa
tensile strength 屈服,23°CASTM D63845.0to65.0 MPa
tensile strength 屈服,23°CISO 527-248.6to62.4 MPa
tensile strength 断裂,23°CISO 527-230.0to141 MPa
tensile strength 23°CASTM D63831.4to173 MPa
elongation屈服,23°CASTM D6383.2to40 %
elongation屈服,23°CISO 527-24.0to5.1 %
elongation断裂,23°CASTM D6382.5to300 %
elongation断裂,23°CISO 527-22.5to55 %
Nominal tensile fracture strain23°CISO 527-217to300 %
Flexural modulus23°CASTM D7901770to8640 MPa
Tensile modulus23°CASTM D6381650to2540 MPa
Tensile modulus23°CISO 527-2275to7950 MPa
Impact resistanceشرایط آزمونروش آزموننتیجه آزمون
Charpy Notched Impact Strength23°CISO 1793.5to12 kJ/m²
Impact strength of simply supported beam without notch23°CISO 17929to96 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25636to81 J/m
Impact strength of cantilever beam gap23°CISO 1803.7to5.3 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D256560to1300 J/m
Impact strength of cantilever beam gap23°CASTM D1822126to945 kJ/m²
Electrical performanceشرایط آزمونروش آزموننتیجه آزمون
dielectric strength23°CIEC 60243-122to37 kV/mm
dielectric constant23°CASTM D1503.48to6.00
Volume resistivity23°CASTM D25755到1.0E+15 ohms·cm
Volume resistivity23°CIEC 600931.0E+10到2.5E+15 ohms·cm
dielectric constant23°CIEC 602504.14
Dissipation Factor23°CASTM D1500.017to0.15
Dissipation Factor23°CIEC 602500.014to0.15
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
Thermal performanceشرایط آزمونروش آزموننتیجه آزمون
melting temperature--ISO 3146200to211 °C
Linear coefficient of thermal expansionMDASTM D6964.9E-5到9.0E-5 cm/cm/°C
Linear coefficient of thermal expansionMDISO 11359-28.6E-5到2.0E-4 cm/cm/°C
Linear coefficient of thermal expansionTDISO 11359-29.0E-5到1.8E-4 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,HDTISO 75-2/A51.7to75.1 °C
vicatISO 306108to201 °C
melting temperature--208to215 °C
melting temperature--ISO 11357-3215to218 °C
Heat distortion temperature0.45MPa,未退火,HDTASTM D648132to212 °C
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B134to172 °C
Heat distortion temperature1.8MPa,未退火,HDTASTM D64854.1to216 °C