PA612 Generic Nylon 612 Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.5to12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 36to81 J/m |
| 23°C | ASTM D1822 | 126to945 kJ/m² | |
| 23°C | ISO 180 | 3.7to5.3 kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 560to1300 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 29to96 kJ/m² |
| hardness | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Rockwell hardness | 23°C | ASTM D785 | 108to115 |
| Electrical performance | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric constant | 23°C | IEC 60250 | 4.14 |
| dielectric strength | 23°C | IEC 60243-1 | 22to37 kV/mm |
| Volume resistivity | 23°C | ASTM D257 | 55到1.0E+15 ohms·cm |
| Dissipation Factor | 23°C | ASTM D150 | 0.017to0.15 |
| 23°C | IEC 60250 | 0.014to0.15 | |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+10到2.5E+15 ohms·cm |
| dielectric constant | 23°C | ASTM D150 | 3.48to6.00 |
| Mechanical properties | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 23.0to296 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 48.6to62.4 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 275to7950 MPa |
| elongation | 屈服,23°C | ISO 527-2 | 4.0to5.1 % |
| 断裂,23°C | ISO 527-2 | 2.5to55 % | |
| Flexural modulus | 23°C | ISO 178 | 1300to2110 MPa |
| tensile strength | 23°C | ASTM D638 | 31.4to173 MPa |
| coefficient of friction | ASTM D1894 | 0.13to1.0 | |
| Tensile modulus | 23°C | ASTM D638 | 1650to2540 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 30.0to141 MPa |
| Flexural modulus | 23°C | ASTM D790 | 1770to8640 MPa |
| elongation | 屈服,23°C | ASTM D638 | 3.2to40 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 17to300 % |
| tensile strength | 屈服,23°C | ASTM D638 | 45.0to65.0 MPa |
| bending strength | 23°C | ISO 178 | 28.5to71.1 MPa |
| elongation | 断裂,23°C | ASTM D638 | 2.5to300 % |
| flammability | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 700to750 °C | |
| Burning wire flammability index | IEC 60695-2-12 | 719to725 °C |
| physical property | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 1.1to1.8 % |
| density | 23°C | ISO 1183 | 1.06to1.07 g/cm³ |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.23to2.0 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 3.0to4.0 % |
| 平衡,23°C,50%RH | ISO 62 | 0.88to1.3 % | |
| density | -- | ASTM D792 | 1.03to1.35 g/cm³ |
| Shrinkage rate | TD:23°C | ASTM D955 | 1.1to2.0 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.13to0.38 % |
| 饱和,23°C | ISO 62 | 2.1to3.0 % |
| Thermal performance | Test Condition | Test Method | Generic/Generic Nylon 612 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 54.1to216 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 132to212 °C | |
| vicat | ISO 306 | 108to201 °C | |
| melting temperature | -- | 208to215 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 134to172 °C |
| melting temperature | -- | ISO 11357-3 | 215to218 °C |
| -- | ISO 3146 | 200to211 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 51.7to75.1 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 4.9E-5到9.0E-5 cm/cm/°C |
| MD | ISO 11359-2 | 8.6E-5到2.0E-4 cm/cm/°C | |
| TD | ISO 11359-2 | 9.0E-5到1.8E-4 cm/cm/°C |