PA12 MN-3020X7 MARPLEX AUSTRALIA
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| melt mass-flow rate | 235°C/2.16kg | ASTM D1238 | 20 g/10min |
| Shrinkage rate | MD | ASTM D955 | 1.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| Rockwell hardness | M-Scale | ASTM D785 | 105 |
| tensile strength | 3.20mm | ASTM D638 | 45.0 MPa |
| elongation | 断裂,3.20mm | ASTM D638 | 200 % |
| Flexural modulus | 3.20mm | ASTM D790 | 1500 MPa |
| bending strength | 3.20mm | ASTM D790 | 59.0 MPa |
| Charpy Notched Impact Strength | ISO 179 | 4.0 kJ/m² | |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 65 J/m |
| density | ASTM D792 | 1.02 g/cm³ | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 92.0 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 47.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.