Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PA12 MN-3020X7 MARPLEX AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Test Condition | Test Method | MARPLEX AUSTRALIA/MN-3020X7 | |
---|---|---|---|
UL flame retardant rating | 1.6mm | UL 94 | HB |
Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 65 J/m |
Rockwell hardness | M级 | ASTM D785 | 105 |
Shrinkage rate | MD | ASTM D955 | 1.0 % |
melt mass-flow rate | 235°C/2.16kg | ASTM D1238 | 20 g/10min |
bending strength | 3.20mm | ASTM D790 | 59.0 MPa |
Flexural modulus | 3.20mm | ASTM D790 | 1500 MPa |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 47.0 °C |
density | ASTM D792 | 1.02 g/cm³ | |
Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |
tensile strength | 3.20mm | ASTM D638 | 45.0 MPa |
elongation | 断裂,3.20mm | ASTM D638 | 200 % |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 92.0 °C |
Charpy Notched Impact Strength | ISO 179 | 4.0 kJ/m² |