PBT TAROLOX 10 G4 Taro Plast S.p.A.

ویژگی‌ها:
Filler
glass fiber reinforced material
20%
filler by weight
مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTMD792	1.45to1.47 g/cm³
Water absorption rate	23°C,24hr	ASTMD570	0.050 %
	Water absorption rate	Saturation	ASTM D570	0.25 %
	Water absorption rate	Water absorption rate	饱和,23°C	ISO 62	0.25 %
GranuleHumidity		内部方法	<0.050 %
melt mass-flow rate	250°C/2.16kg	ASTMD1238	20 g/10min
Shrinkage rate	MD	ASTM D955	0.40to0.60 %
Shrinkage rate	Shrinkage rate	TD	ASTM D955	0.60to1.0 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	120

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.0mm	UL 94	HB
	UL flame retardant rating	1.6mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	650 °C
Limiting Oxygen Index		ASTM D2863	20 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Break	ASTMD638	3.0 %
Flexural modulus		ASTMD790	6500 MPa
bending strength	--	ISO 178	155 MPa
bending strength	bending strength	Break	ASTM D790	155 MPa
Tensile modulus		ASTMD638	7000 MPa
tensile strength	Break	ASTMD638	105 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179	6.5 kJ/m²
Impact strength of cantilever beam gap	-20°C,3.20mm	ASTMD256	60 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	70 J/m

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	PLC 1
Compared to the Leakage Tracking Index (CTI)	Compared to the Leakage Tracking Index (CTI)	解决方案B	IEC 60112	PLC 3
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
dielectric strength	2.00mm	ASTM D149	23 kV/mm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火，HDT	ASTMD648	218 °C
Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火，HDT	ASTMD648	205 °C
Continuous use temperature	--3	IEC 60216	90.0 °C
ball-indentation hardness	205°C	VDE0470	通过
melting temperature		ASTMD211	220to225 °C
Linear coefficient of thermal expansion	MD：-30到30°C	ASTM D696	3.5E-05 cm/cm/°C
Continuous use temperature	--4	IEC 60216	130 °C
	Continuous use temperature	--5	IEC 60216	130 °C
	Continuous use temperature	Continuous use temperature	--6	IEC 60216	180 °C
vicat	--	ASTMD15257	216 °C
vicat	vicat	--	ASTMD15258	210 °C