PBT TAROLOX 10 G4 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 6.5 kJ/m² |
Impact strength of cantilever beam gap | -20°C,3.20mm | ASTMD256 | 60 J/m |
23°C,3.20mm | ASTMD256 | 70 J/m |
hardness | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 120 |
Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Flexural modulus | ASTMD790 | 6500 MPa | |
elongation | 断裂 | ASTMD638 | 3.0 % |
bending strength | 断裂 | ASTM D790 | 155 MPa |
Tensile modulus | ASTMD638 | 7000 MPa | |
tensile strength | 断裂 | ASTMD638 | 105 MPa |
bending strength | -- | ISO 178 | 155 MPa |
Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
dielectric strength | 2.00mm | ASTM D149 | 23 kV/mm |
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
解决方案B | IEC 60112 | PLC 3 |
flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
UL flame retardant rating | 1.0mm | UL 94 | HB |
3.2mm | UL 94 | HB | |
1.6mm | UL 94 | HB | |
Limiting Oxygen Index | ASTM D2863 | 20 % |
physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
melt mass-flow rate | 250°C/2.16kg | ASTMD1238 | 20 g/10min |
Water absorption rate | 饱和 | ASTM D570 | 0.25 % |
Shrinkage rate | MD | ASTM D955 | 0.40to0.60 % |
GranuleHumidity | 内部方法 | <0.050 % | |
density | ASTMD792 | 1.45to1.47 g/cm³ | |
Water absorption rate | 23°C,24hr | ASTMD570 | 0.050 % |
饱和,23°C | ISO 62 | 0.25 % | |
Shrinkage rate | TD | ASTM D955 | 0.60to1.0 % |
Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROLOX 10 G4 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTMD648 | 205 °C |
0.45MPa,未退火,HDT | ASTMD648 | 218 °C | |
Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 3.5E-05 cm/cm/°C |
Continuous use temperature | --3 | IEC 60216 | 90.0 °C |
ball-indentation hardness | 205°C | VDE0470 | 通过 |
Continuous use temperature | --5 | IEC 60216 | 130 °C |
--4 | IEC 60216 | 130 °C | |
melting temperature | ASTMD211 | 220to225 °C | |
vicat | -- | ASTMD15257 | 216 °C |
Continuous use temperature | --6 | IEC 60216 | 180 °C |
vicat | -- | ASTMD15258 | 210 °C |