| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| yield | 1.03to33.45 Mpa | ||
| Nominal tensile fracture strain | 23℃ | % | 2.5to500 |
| fracture | 14.0to64.0 Mpa | ||
| yield | 4.0to51.03 Mpa | ||
| transmissivity | % | 88.9to93.1 | |
| fracture | % | 550to850 | |
| yield | 1.7to33.03 Mpa | ||
| fracture | % | 400to890 | |
| Haze ratio | % | 0.20to3.1 | |
| Maximum continuous use temperature | °C | 150to170 | |
| burning rate | mm/min | 38.1to53.34 | |
| brittle temperature | °C | -60--59 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 59to62 |
| Impact strength of cantilever beam gap | 23℃ | J/m | 0.007to0.037 |
| Dart impact | 23℃ | N.m | 47.17to3256.64 |
| Charpy Notched Impact Strength | 23℃ | kJ/m² | 0.353to2.182 |
| yield | % | 2.0to2.1 | |
| compression set | 23℃ | % | 18to36 |
| fracture | 3.97to20.34 Mpa | ||
| yield | 24.41to54.0 Mpa | ||
| Melt volume flow rate | 200°C/5.0kg | cm³/10min | 0.04to0.05 |
| flow | mm/mm | 152.4E-3-172.7E-3 | |
| fracture | % | 30to260 |