physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Water absorption rate | 23°C,24hr | ASTMD570 | 0.60 % |
Water absorption rate | Saturation | ASTM D570 | 4.5 % |
Water absorption rate | 饱和,23°C | ISO 62 | 4.5 % |
GranuleHumidity | | 内部方法 | <0.15 % |
density | | ASTMD792 | 1.39to1.41 g/cm³ |
melt mass-flow rate | 280°C/2.16kg | ASTMD1238 | 15 g/10min |
Shrinkage rate | MD | ASTM D955 | 0.25to0.35 % |
Shrinkage rate | TD | ASTM D955 | 0.70to0.90 % |
hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Rockwell hardness | R-Scale | ASTM D785 | 122 |
flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
UL flame retardant rating | 1.0mm | UL 94 | HB |
Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
Limiting Oxygen Index | | ASTM D2863 | 27 % |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
bending strength | Break | ASTM D790 | 270 MPa |
Tensile modulus | | ASTMD638 | 10500 MPa |
tensile strength | Break | ASTMD638 | 190 MPa |
elongation | Break | ASTMD638 | 2.0 % |
Flexural modulus | | ASTMD790 | 10000 MPa |
bending strength | -- | ISO 178 | 270 MPa |
Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 60 kJ/m² |
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 130 J/m |
Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
Volume resistivity | | ASTM D257 | 8E+15 ohms·cm |
dielectric strength | 2.00mm | ASTM D149 | 26 kV/mm |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 2.6E-05 cm/cm/°C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTMD648 | 246 °C |
Continuous use temperature | --3 | IEC 60167 | 100 °C |
Continuous use temperature | --4 | IEC 60216 | 130 °C |
Continuous use temperature | --5 | IEC 60216 | 140 °C |
Continuous use temperature | --6 | IEC 60216 | 180 °C |
vicat | | ISO 306/B50 | 255 °C |
ball-indentation hardness | 165°C | VDE0470 | 通过 |
melting temperature | | ASTMD211 | 256 °C |