PA66 TAROMID A 280 G8 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 130 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 60 kJ/m² |
| hardness | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 122 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Flexural modulus | ASTMD790 | 10000 MPa | |
| elongation | 断裂 | ASTMD638 | 2.0 % |
| bending strength | 断裂 | ASTM D790 | 270 MPa |
| Tensile modulus | ASTMD638 | 10500 MPa | |
| tensile strength | 断裂 | ASTMD638 | 190 MPa |
| bending strength | -- | ISO 178 | 270 MPa |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 8E+15 ohms·cm | |
| dielectric strength | 2.00mm | ASTM D149 | 26 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 750 °C |
| UL flame retardant rating | 1.0mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 27 % |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 4.5 % |
| Shrinkage rate | MD | ASTM D955 | 0.25to0.35 % |
| GranuleHumidity | 内部方法 | <0.15 % | |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.60 % |
| density | ASTMD792 | 1.39to1.41 g/cm³ | |
| Water absorption rate | 饱和,23°C | ISO 62 | 4.5 % |
| Shrinkage rate | TD | ASTM D955 | 0.70to0.90 % |
| melt mass-flow rate | 280°C/2.16kg | ASTMD1238 | 15 g/10min |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 G8 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 246 °C |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 2.6E-05 cm/cm/°C |
| Continuous use temperature | --5 | IEC 60216 | 140 °C |
| --4 | IEC 60216 | 130 °C | |
| vicat | ISO 306/B50 | 255 °C | |
| ball-indentation hardness | 165°C | VDE0470 | 通过 |
| melting temperature | ASTMD211 | 256 °C | |
| Continuous use temperature | --6 | IEC 60216 | 180 °C |
| --3 | IEC 60167 | 100 °C |