Polyolefin, Unspecified PRE-ELEC® CP 1316 Premix Oy

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.11 g/cm³
density	density		ISO 1183	1.12 g/cm³
melt mass-flow rate	190°C/21.6kg	ISO 1133	12 g/10min
Shrinkage rate	MD	ASTM D955	0.12 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.2 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	Shore A	ISO 868	93
Shore hardness	Shore hardness	邵氏D	ISO 868	43

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	4.00mm	ISO 527-2	11.0 MPa
Tensile strain	断裂,4.00mm	ISO 527-2	500 %
Flexural modulus	4.00mm	ASTM D790	1100 MPa
Flexural modulus	Flexural modulus	4.00mm	ISO 178	110 MPa
tensile strength		ASTM D638	11.0 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	-20°C2	ASTM D256	40 kJ/m²
	Charpy Notched Impact Strength	-20°C3	ISO 179	40 kJ/m²
		Charpy Notched Impact Strength	23°C3	ISO 179	NoBreak
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C2	ASTM D256	NoBreak
Impact strength of simply supported beam without notch	-20°C	ASTM D256	NoBreak
	Impact strength of simply supported beam without notch	-20°C	ISO 179	NoBreak
		Impact strength of simply supported beam without notch	2°C	ISO 179	NoBreak
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ASTM D256	NoBreak
Impact strength of cantilever beam gap	-20°C,4.00mm，Area	ASTM D256	NoBreak
	Impact strength of cantilever beam gap	23°C,4.00mm，Area	ASTM D256	NoBreak
		Impact strength of cantilever beam gap	-20°C	ISO 180	NoBreak
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	NoBreak
Suspended wall beam without notch impact strength	-20°C,4.00mm	ASTM D256	NoBreak
	Suspended wall beam without notch impact strength	23°C,4.00mm	ASTM D256	NoBreak
		Suspended wall beam without notch impact strength	-20°C	ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		ESDSTM11.11	<1.0E+3 ohms
Surface Resistivity	Surface Resistivity		IEC 61340-2-3	<1.0E+3 ohms
Volume resistivity		内部方法	<1.0E+2 ohms·cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
vicat		ASTM D15254	50.0 °C
vicat	vicat		ISO 306/A50	50.0 °C
Heat distortion temperature	0.45MPa,未退火，HDT	ASTM D648B	35.0 °C
Heat distortion temperature	Heat distortion temperature	0.45MPa,未退火，HDT	ISO 75-2/Bf	35.0 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.