Polyolefin, Unspecified PRE-ELEC® CP 1316 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,4.00mm，Area | ASTM D256 | NoBreak |
| Impact strength of simply supported beam without notch | 2°C | ISO 179 | NoBreak |
| Charpy Notched Impact Strength | 23°C3 | ISO 179 | NoBreak |
| Suspended wall beam without notch impact strength | -20°C,4.00mm | ASTM D256 | NoBreak |
| Impact strength of simply supported beam without notch | 23°C | ASTM D256 | NoBreak |
| -20°C | ASTM D256 | NoBreak | |
| -20°C | ISO 179 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | -20°C2 | ASTM D256 | 40 kJ/m² |
| Suspended wall beam without notch impact strength | -20°C | ISO 180 | NoBreak |
| 23°C | ISO 180 | NoBreak | |
| Charpy Notched Impact Strength | 23°C2 | ASTM D256 | NoBreak |
| Impact strength of cantilever beam gap | -20°C,4.00mm，Area | ASTM D256 | NoBreak |
| Charpy Notched Impact Strength | -20°C3 | ISO 179 | 40 kJ/m² |
| Impact strength of cantilever beam gap | -20°C | ISO 180 | NoBreak |
| Suspended wall beam without notch impact strength | 23°C,4.00mm | ASTM D256 | NoBreak |
| hardness | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 43 |
| 邵氏A | ISO 868 | 93 |
| Mechanical properties | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| tensile strength | ASTM D638 | 11.0 MPa | |
| Tensile strain | 断裂,4.00mm | ISO 527-2 | 500 % |
| Flexural modulus | 4.00mm | ASTM D790 | 1100 MPa |
| 4.00mm | ISO 178 | 110 MPa | |
| tensile strength | 4.00mm | ISO 527-2 | 11.0 MPa |
| Electrical performance | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| Surface Resistivity | ESDSTM11.11 | <1.0E+3 ohms | |
| IEC 61340-2-3 | <1.0E+3 ohms | ||
| Volume resistivity | 内部方法 | <1.0E+2 ohms·cm |
| physical property | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.12 % |
| MD | ISO 294-4 | 1.2 % | |
| density | ASTM D792 | 1.11 g/cm³ | |
| ISO 1183 | 1.12 g/cm³ | ||
| melt mass-flow rate | 190°C/21.6kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | Premix Oy/PRE-ELEC® CP 1316 |
|---|---|---|---|
| vicat | ISO 306/A50 | 50.0 °C | |
| ASTM D15254 | 50.0 °C | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648B | 35.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/Bf | 35.0 °C |