impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-20°C	ISO 179/1eA	2.4	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	8.0	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	25	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	750	°C
Extreme Oxygen Index		ASTM D2863	26	%
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	750	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Yield,90°C	ISO 527-2/5	6.5	%
	Tensile strain	Break,23°C	ISO 527-2/5	8.0	%
		Tensile strain	Break,60°C	ISO 527-2/5	12	%
		Tensile strain	Tensile strain	Break,90°C	ISO 527-2/5	20	%
tensile strength	Break,60°C	ISO 527-2/5	10.0	MPa
tensile strength	tensile strength	Break,90°C	ISO 527-2/5	7.00	MPa
Tensile strain	Yield,23°C	ISO 527-2/5	2.5	%
Tensile strain	Tensile strain	Yield,60°C	ISO 527-2/5	6.0	%
Tensile modulus	23°C	ISO 527-2/1	3200	MPa
tensile strength	Yield,23°C	ISO 527-2/5	25.0	MPa
	tensile strength	Yield,60°C	ISO 527-2/5	20.0	MPa
		tensile strength	Yield,90°C	ISO 527-2/5	10.0	MPa
		tensile strength	tensile strength	Break,23°C	ISO 527-2/5	15.0	MPa
Tensile modulus	60°C	ISO 527-2/1	1400	MPa
Tensile modulus	Tensile modulus	90°C	ISO 527-2/1	950	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0	°C
	Hot deformation temperature	Hot deformation temperature	连续使用温度4		105	°C
Vicat softening temperature		ISO 306/B50	75.0	°C
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	3.5E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	TD:2.00mm	ISO 294-4	0.70to1.0	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	0.75to1.0	%
Water absorption rate	23°C,24hr	ISO 62	0.050	%
density		ISO 1183	1.32	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0