برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| water content | | ISO 960 | <2000 ppm |
| density | | ISO 1183 | 1.23 g/cm³ |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.3 % |
| density | | ISO 1183 | 1.23 g/cm³ |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.3 % |
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| UL flame retardant rating | 1.60 mm | UL 94 | HB |
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 °C |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/5 | 5750 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Tensile modulus | 23°C | ISO 527-2/5 | 5750 MPa |
| tensile strength | 断裂, 23°C | ISO 527-2/5 | 120.0 MPa |
| Tensile strain | 断裂, 23°C | ISO 527-2/5 | 3.0 % |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| melting temperature | | ISO 11357 | 262 °C |
| vicat | | ISO 306/B | 245 °C |
| melting temperature | | ISO 11357 | 262 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 245 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 240 °C |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 245 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 240 °C |
| vicat | | ISO 306/B | 245 °C |