PC LNP™ LUBRICOMP™ DFL36EU compound SABIC

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	24hr,50%RH	ASTM D570	0.080 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.11 %
density		ASTM D792	1.56 g/cm³
density	density		ASTM D792	1.56 g/cm³
Shrinkage rate	MD：24小时	ASTM D955	0.10to0.30 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	0.50to0.70 %

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	9230 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	8690 MPa
tensile strength	Break	ASTM D638	116 MPa
tensile strength	tensile strength	Break	ISO 527-2/5	113 MPa
elongation	Break	ASTM D638	2.7 %
Tensile strain	Break	ISO 527-2/5	2.6 %
Flexural modulus	50.0mm跨距	ASTM D790	8910 MPa
Flexural modulus	Flexural modulus		ISO 178	8340 MPa
Wear factor	Washer	ASTM D3702Modified	30.0 10^-10in^5-min/ft-lb-hr
bending strength		ISO 178	175 MPa
	bending strength	屈服,50.0mm跨距	ASTM D790	190 MPa
	bending strength	bending strength	断裂,50.0mm跨距	ASTM D790	189 MPa
coefficient of friction	Dynamic	ASTM D3702Modified	0.47
coefficient of friction	coefficient of friction	Static	ASTM D3702Modified	0.51
Wear factor	Ring	ASTM D3702Modified	2.00 10^-10in^5-min/ft-lb-hr

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Multi axis Instrumented Impact Energy		ISO 6603-2	5.30 J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	51 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	16.9 J
Impact strength of cantilever beam gap	23°C	ASTM D256	170 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	710 J/m

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD：-30到30°C	ASTM D696	5.4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	4.3E-05 cm/cm/°C
Heat distortion temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	146 °C
	Heat distortion temperature	0.45MPa,Unannealed,64.0mmSpan，HDT	ISO 75-2/Bf	145 °C
		Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	141 °C
		Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,64.0mm跨距，HDT	ISO 75-2/Af	141 °C