برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Apparent density | | | 0.70 g/cm³ |
| Melt volume flow rate | 325°C/5.0 kg | ISO 1133 | 45.0 cm3/10min |
| Shrinkage rate | 横向流量 | ISO 294-4 | 0.70 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 4.3 to 5.3 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.4 to 1.8 % |
| viscosity number | 96% H2SO4 | ISO 307 | 120 cm³/g |
| Mold Shrinkage - Model Heating | 1.50 mm | | 0.10 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Burning wire flammability index | 0.40 mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 50 % |
| Polymer Abbreviation | | | PA6T/6-GF30 FR |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 11000 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 150 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 11000 Mpa |
| bending strength | | ISO 178 | 240 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | 1.0E+17 ohms·cm |
| relative permittivity | 1 MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 110 °C |
| drying time | | | 8.0 hr |
| Suggested maximum moisture content | | | 0.030 % |
| Hopper temperature | | | 80 °C |
| Temperature at the rear of the barrel | | | 300 °C |
| Temperature in the middle of the barrel | | | 310 °C |
| Temperature at the front of the material cylinder | | | 320 °C |
| Spray nozzle temperature | | | 320 °C |
| Processing (melt) temperature | | | 310 to 330 °C |
| Temperature | | | 80 to 120 °C |
| Residence Time | | | < 5.0 min |
| screw speed | | | < 18 m/min |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 220 °C |
| melting temperature | | ISO 11357-3 | 290 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.