PC LNP™ THERMOCOMP™ D452 compound SABIC

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD:24小时	ASTM D955	0.10to0.25 %
Shrinkage rate	Shrinkage rate	TD:24小时	ASTM D955	0.10to0.25 %
density		ASTM D792	1.52 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17 g/10min
melt mass-flow rate	melt mass-flow rate	300°C/2.16kg	ASTM D1238	39 g/10min
Melt volume flow rate	300°C/1.2kg	ISO 1133	12.0 cm³/10min
Melt volume flow rate	Melt volume flow rate	300°C/2.16kg	ISO 1133	30.0 cm³/10min

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.00mm	UL 94	V-0

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	41 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	150 J/m
Suspended wall beam without notch impact strength	23°C	ASTM D4812	620 J/m

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
fracture		ASTM D638	141 MPa
	fracture		ISO 527-2/5	140 MPa
		fracture		ASTM D638	2.3 %
			fracture		ISO 527-2/5	2.2 %
			fracture	fracture		ASTM D790	211 MPa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	98.0 °C
Linear coefficient of thermal expansion	MD:23到80°C	ISO 11359-2	1.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:23到80°C	ISO 11359-2	5.8E-05 cm/cm/°C