برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.06 g/cm³ |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 20.0 cm³/10min |
| Shrinkage rate | TD | ISO 2577 | 0.50 % |
| Shrinkage rate | MD | ISO 2577 | 0.50 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ball-indentation hardness | | ISO 2039-1 | 106 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2550 MPa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 50.5 MPa |
| tensile strength | 断裂,23°C | ISO 527-2/50 | 36.5 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.6 % |
| Flexural modulus | 23°C | ISO 178 | 2600 MPa |
| bending strength | 23°C | ISO 178 | 75.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | >15 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 20 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 100 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 120 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 2E+17 ohms |
| Volume resistivity | | IEC 60093 | 2E+16 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.04 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 2.82 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5.3E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 9.6E-03 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 7.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 98.0 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 94.0 °C |
| vicat | -- | ISO 306/B50 | 98.0 °C |
| vicat | -- | ISO 306/B120 | 101 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.