ABS ELIX™ ABS M205FC ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 16 kJ/m² |
-30°C | ISO 179/1eA | 7.0 kJ/m² | |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 120 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 100 kJ/m² |
hardness | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 106 MPa |
Electrical performance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
relative permittivity | 23°C,1MHz | IEC 60250 | 2.82 |
23°C,100Hz | IEC 60250 | 3.04 | |
Surface Resistivity | IEC 60093 | 2E+17 ohms | |
Dissipation Factor | 23°C,100Hz | IEC 60250 | 5.3E-03 |
23°C,1MHz | IEC 60250 | 9.6E-03 |
Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
tensile strength | 屈服,23°C | ISO 527-2/50 | 50.5 MPa |
Flexural modulus | 23°C | ISO 178 | 2600 MPa |
Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.6 % |
tensile strength | 断裂,23°C | ISO 527-2/50 | 36.5 MPa |
Tensile strain | 断裂,23°C | ISO 527-2/50 | >15 % |
Nominal tensile fracture strain | 23°C | ISO 527-2/50 | 20 % |
Tensile modulus | 23°C | ISO 527-2/1 | 2550 MPa |
bending strength | 23°C | ISO 178 | 75.0 MPa |
flammability | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
Shrinkage rate | TD | ISO 2577 | 0.50 % |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 20.0 cm³/10min |
Shrinkage rate | MD | ISO 2577 | 0.50 % |
density | ISO 1183 | 1.06 g/cm³ |
Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./ELIX™ ABS M205FC |
---|---|---|---|
vicat | -- | ISO 306/B120 | 101 °C |
Linear coefficient of thermal expansion | MD:23到55°C | ISO 11359-2 | 7.8E-05 cm/cm/°C |
TD:23to55°C | ISO 11359-2 | 8.1E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 94.0 °C |
vicat | -- | ISO 306/B50 | 98.0 °C |
Heat distortion temperature | 0.45MPa,退火,HDT | ISO 75-2/B | 98.0 °C |