PCT Infino TK-2050HL LOTTE KOREA

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.77 g/cm³
density	density		ISO 1183	1.77 g/cm³
melt mass-flow rate	300°C/2.16kg	ASTM D1238	15 g/10min
melt mass-flow rate	melt mass-flow rate	300°C/2.16kg	ISO 1133	15 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.54 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.56 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.56 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.54 %
ash content	--	ISO 3451	51 %
ash content	ash content	--	ASTM D5630	51 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	111
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	111

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.530mm	UL 94	HB

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	4060 MPa
Tensile modulus	Tensile modulus		ISO 527-2/5	4100 MPa
tensile strength	Yield	ASTM D638	58.8 MPa
	tensile strength	Yield	ISO 527-2/5	56.0 MPa
		tensile strength	Break	ASTM D638	58.8 MPa
		tensile strength	tensile strength	Break	ISO 527-2/5	56.0 MPa
elongation	Break	ASTM D638	2.1 %
bending strength		ASTM D790	90.2 MPa
bending strength	bending strength		ISO 178	80.0 MPa
Tensile strain	Break	ISO 527-2/5	2.1 %
Flexural modulus		ASTM D790	6080 MPa
Flexural modulus	Flexural modulus		ISO 178	5200 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	-5°C	ISO 180/1U	16 kJ/m²
Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	27 J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	3.6 kJ/m²
		Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	250 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	200 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	22 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	29 J/m

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火,6.40mm，HDT	ASTM D648	250 °C
	Heat distortion temperature	0.45MPa,Unannealed,4.00mm，HDT	ISO 75-2/B	250 °C
		Heat distortion temperature	1.8MPa,未退火,6.40mm，HDT	ASTM D648	202 °C
		Heat distortion temperature	Heat distortion temperature	1.8MPa,Unannealed,4.00mm，HDT	ISO 75-2/A	202 °C