PPO(PPE)+PS+PP NORYL PPX™ PPX640F resin SABIC

ویژگی‌ها:
Filler glass fiber reinforced material 40% filler by weight
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	110 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	580 J/m
Dart impact	-30°C,TotalEnergy	ASTM D3763	14.1 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	16.8 J
Impact strength of cantilever beam gap	-30°C	ASTM D256	96 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ASTM D638	95.8 MPa
tensile strength	tensile strength	Break	ASTM D638	95.8 MPa
elongation	Break	ASTM D638	6.4 %
Bending modulus	50.0mmSpan	ASTM D790	8320 MPa
bending strength	Break,50.0mmSpan	ASTM D790	151 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.3E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	159 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	146 °C
Vicat softening temperature		ASTM D15254	163 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1.1E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.30 g/cm³
melt mass-flow rate	260°C/5.0kg	ASTM D1238	1.3 g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.17to0.18 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	Internal Method	0.27to0.61 %