| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 235°C/2.16 kg | ISO 1133 | 11.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.6 % |
| Water absorption rate | 饱和 | ASTM D570 | 1.1 % |
| Shore hardness | | ASTM D785 | 78 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flammability level | | UL 94 | HB |
| Flammability level | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 405 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 27.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 42 % |
| Nominal tensile fracture strain | | ISO 527-2 | > 50 % |
| Fracture tensile strength | 断裂 | ASTM D638 | 64.1 Mpa |
| elongation | 断裂 | ASTM D638 | 430 % |
| Flexural modulus | | ASTM D790 | 338 Mpa |
| Impact strength of cantilever beam gap | | ASTM D256 | 320 J/m |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | -- |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | -- |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | -- ohms |
| Volume resistivity | | IEC 60093 | -- ohms·cm |
| dielectric strength | | IEC 60243-1 | -- KV/mm |
| relative permittivity | 100 Hz | IEC 60250 | 10.0 |
| relative permittivity | 1 MHz | IEC 60250 | 4.00 |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.18 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.096 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | V |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 130 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 45.0 °C |
| vicat | | ISO 306/B50 | 140 °C |
| melting temperature | | ISO 11357-3 | 182 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| melting temperature | | DSC | 186 °C |
| Heat distortion temperature | 1.8MPa，HDT | QJ/CL.4.3.19 | 41.1 °C |