| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| Shrinkage rate | MD | ASTM D955 | 0.40to0.70 % |
| Shrinkage rate | TD | ASTM D955 | 0.40to0.70 % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.10 % |
| Water absorption rate | Saturation | ASTM D570 | 0.40 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.7mm | UL 94 | V-0 |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Yield | ASTMD638 | 50.0 MPa |
| Flexural modulus | | ASTMD790 | 2100 MPa |
| bending strength | --3 | ISO 178 | 70.0 MPa |
| bending strength | Yield | ASTM D790 | 70.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 20 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Impact strength of cantilever beam gap | | ASTMD256 | 500 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 110 °C |
| vicat | -- | ASTMD15255 | 135 °C |
| vicat | -- | ASTMD15256 | 125 °C |
| ball-indentation hardness | 125°C | VDE0470 | 通过 |