ABS MAGNUM™ 1150 EM Trinseo
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.03 g/cm³ | |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 0.90 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.60to0.70 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | 3.20mm | ASTM D638 | 1750 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 36.5 MPa |
| Tensile strain | Yield,3.20mm | ASTM D638 | 3.0 % |
| elongation | 断裂,3.20mm | ASTM D638 | 30 % |
| Flexural modulus | 3.20mm | ASTM D790 | 1980 MPa |
| bending strength | 3.20mm | ASTM D790 | 58.9 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | -29°C,3.20mm | ASTM D256 | 340 J/m |
| 23°C,3.20mm | ASTM D256 | 560 J/m | |
| Dart impact | -29°C,3.20mm,PeakEnergy | ASTM D3763 | 32.8 J |
| -29°C,3.20mm,TotalEnergy | ASTM D3763 | 42.9 J | |
| 23°C,3.20mm,PeakEnergy | ASTM D3763 | 29.9 J | |
| 23°C,3.20mm,TotalEnergy | ASTM D3763 | 45.2 J |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 96.1 °C |
| 0.45MPa,Annealed,3.20mm，HDT | ASTM D648 | 111 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 82.2 °C | |
| 1.8MPa,退火,3.20mm，HDT | ASTM D648 | 108 °C | |
| vicat | ASTM D1525 | 112 °C | |
| Linear coefficient of thermal expansion | MD：3.20mm | ASTM D696 | 9.5E-05 cm/cm/°C |