| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 20.0 cm³/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 总计,4000µm | ISO 13468 | 88.0 % |
| Haze ratio | 1000µm3 | ISO 13468 | 79 % |
| Haze ratio | 2000µm2 | ISO 13468 | 92 % |
| Haze ratio | 3000µm2 | ISO 13468 | 92 % |
| transmissivity | 总计,1000µm | ISO 13468 | 89.5 % |
| transmissivity | 总计,2000µm | ISO 13468 | 88.7 % |
| transmissivity | 总计,3000µm | ISO 13468 | 88.5 % |
| Haze ratio | 4000µm2 | ISO 13468 | 93 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | 4.0mm | IEC 60695-2-12 | 850 °C |
| FireBehavior,FMVSS | 1.00mm | ISO 37 | passed |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| half-power angle | 1.00mm | | 3.00 ° |
| half-power angle | 2.00mm | | 8.00 ° |
| half-power angle | 3.00mm | | 10.0 ° |
| half-power angle | 4.00mm | | 11.0 ° |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2 | 2400 MPa |
| tensile strength | Yield | ISO 527-2 | 66.0 MPa |
| tensile strength | -- | ISO 527-2 | 66.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 6.0 % |
| Tensile strain | Break | ISO 527-2 | 70 % |
| Flexural modulus | | ISO 178 | 2450 MPa |
| bending strength | 3.5%应变 | ISO 178 | 76.0 MPa |
| bending strength | -- | ISO 178 | 100 MPa |
| FlexuralDeflectionMaxForce | | ISO 178 | 7.0 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | -- | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | -20°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | -- | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | -20°C | ISO 179/1eU | 无断裂 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ISO 306/B50 | 142 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 124 °C |